Worldinmfg can provide most competitive Light-weight Insulation Silica Refractory Brick For Glass Furnace, Coke Oven,

Light-weight Insulation Silica Refractory Brick For Glass Furnace, Coke Oven

  • Light-weight Insulation Silica Refractory Brick For Glass Furnace, Coke Oven
  • Light-weight Insulation Silica Refractory Brick For Glass Furnace, Coke Oven

Light-weight Insulation Silica Refractory Brick For Glass Furnace, Coke Oven

Unit Price:   Get Latest Price

Packaging: packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages
 

Mr.Jacky Liu
Other

Product Description

Light-weight Insulation Silica Refractory Brick For Glass Furnace, Coke Oven

 

Description:

Laurel can produces a large range of silica brick for many kind of industry usage.

SiO2 content: Above 95%.
Al2O3 content: Below 1.0%.
Usage: Hot-blast stove.
Our factory product various kinds of refractory products. The products can be made according with the customers' requirement.

 

Features:

  1. Silicon oxide is above 95%.
  2. Good acid erosion resistance.
  3. High softening point with temperature.
  4. No shrink in burn repeatedly.
  5. Temperature of refractoriness under load is above 1650º C

 

Applications:

  1. Glass furnace
  2. Coke oven
  3. Blast furnace

 

Specifications:

Technical data

Silica brick for glass furnace

Item:

GF-96A

GF-96B

GF-95A

GF-95B

SiO 2

≥96

≥96

≥95

≥95

Fe 2 O 3

≤0.8

≤1.0

≤1.2

≤1.2

Apparent porosity %

≤22(24)

Cold Crushing

Strength MPa

Brick below20KG

≥35(30)

Brick ≥20KG

≥30(25)

Refractoriness under load ºC

≥1680

≥1670

≥1660

≥1650

True density g/cm ³

≤2.34

≤2.34

≤2.35

≤2.35

Silica brick for coke oven

Item:

CO-94A

CO-94B

SiO2: %

≥94

≥94

Al 2 O 3 : %

≤ 1.5

≤ 1.5

Fe2O3: %

≤ 1.5

≤ 1.5

Refractoriness under load 0.2Mpa

≥ 1650ºC

≥ 1650ºC

Apparent porosity: %

≤ 22

≤ 24

Bulk density: g/cm ³

≤ 2.34

≤ 2.35

Cold crushing strength: MPa

≥30

≥25

Permanent linear change % (1450ºC ×2h)

0~0.2

0~0.2

Thermal expansion(1000ºC)

≤1.28

≤1.30

Silica brick for hot blast furnace

Item

HBF-95

SiO2

≥ 95

Al2O3

≤ 1.0

Fe2O3

≤1.3

Apparent porosity %

≤22(24)

Cold crushing strength MPa

≥45(35)

Remaining quarts %

≤1.0

Refractoriness under load ºC

≥1650

Creep(0.2Mpa ×1550ºC×50h) %

≤0.8

Thermal expansion coefficient (1000ºC) %

≤1.25

Apparent density g/cm ³

≤2.32

 

Competitive Advantage:

  1. Competitive Price. Make the products competitive in your market.
  2. Abundant Experience. Prevent cracks and twist in bricks.
  3. Different Moulds. Save mould fees for you.
  4. Strict Quality Control. Meet clients’ quality requirement.
  5. Large stocks. Guarantee prompt delivery.
  6. Professional Packing. Avoid damage and secure the goods in transportation

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

More special shapes of firebrick


How to pack


Our plant


You could mix loading the container to save cost


Our team


Customers

Email to this supplier
  • *Subject:
  • *Messages:
    Your message must be between 20-8000 characters
Other products from this supplier
Featured Products

Caustic Calcined Magnesite Briquettes

Origin: China

Min. Order:

Dead Burned Magnesite

Origin: China

Min. Order:

Large Crystal Electro-Fused Magnesite

Origin: China

Min. Order:

Alumina Brick

Origin: China

Min. Order:

SYNTHETIC MAGNESITE-CHROME SINTER

Origin: china

Min. Order:

aluminum silicate ceramic fiber blanket

Origin:

Min. Order: